Silicone Silicate Render EWI-040


Silicone Silicate Render is our most popular hybrid silicone render, offering great performance and great value. Silicone Silicate is fantastically versatile, providing the key benefits of a thin coat render with the added boost of self-cleaning and breathability that the silicone technology provides. Silicone Silicate is perfect for a standard classic finish that will maintain its brilliance in the long term. Available in a range of grain sizes for a textured finish, including 1mm, 1.5mm, 2mm and 3mm.
View Safety Data Sheet
View Product Data Sheet

SKU: N/A Category:

Intended Uses

Unlike our dry-mix renders, this is a ready-to-use render. It is very versatile as it is suitable for use on brick, concrete, traditional plasters, gypsum substrates and chipboard. The render is a mixture of potassium water glass, silicone emulsions and pigments. Silicone Silicate Render is also available in hundreds of colours, catering to every taste.

Application Conditions

  • Application and setting temperature: from +5°C to +25°C.
  • Silicone Silicate Render should be applied in temperate weather and should not be used in temperatures above 30°C. Likewise, if the materials or the substrate are frozen, or if there is any risk of frost damage within the first 24 hours, work should be postponed.
  • Silicone Silicate Render should not be applied in rain or humid conditions, or if wet weather is expected before the render has set.
  • Setting time is typically 12-48 hours, although this is dependent upon environment and humidity.

Additional information


Acorn, Almond, Antique White, Ash, Bone, Clay, Cloud, Concrete, Copenhagen, Diamond, Eggshell, Elderflower, Fog, Frost, Haze, Ice, Ivory, Lead, Linen, Magnolia, Mirror, Mist, Opal, Orchid, Paraffin, Platinum, Porcelain, Prosecco, Pure White, Sage Green, Sandstone, Silk, Silver, Smoke, Storm, Truffle


There are no reviews yet.

Be the first to review “Silicone Silicate Render EWI-040”

Your email address will not be published. Required fields are marked *